Multilayer® 3D

Gradual hardness & Gradual translucency & Gradual color
3D multilayer realizes natural gradient of color,gradient of translucency and gradient of strength in a real sense, achieving another revolution of dental material and revolutionizing dentistry once again！

Color gradient:

6 layers of natural color transition, matching color gradient of natural tooth from cervical to incisal.

Translucency gradient:

Translucency from 57% in incisal to 43% in cervical.It shows gradient decrease,achieving life-like transparency of natural tooth enamel while low transparency in cervical has effective opaque！

Strength gradient:

Strength gradient from 600 Mpa to 900 Mpa. It achieves low strength in occlusion and causes no harm to opposing dentin. High strength in base part realizes long bridge restoration！

Indications:

1) Anterior full contour (crown &bridge)
2) Posterior full contour (crown &bridge)

Color classification:

1) A1 A2 A3 A3.5 A4
2) B1 B2 B3 B4
3) C1 C2 C3 C4
4) D2 D3 D4

Chemical composition and Mechanical property:

1) Sintered Density ≥6g/cm³
2) Fracture Toughness =5Mpam½
3) Hardness(Hv 10) =1250

Flexural strength:

percentage thickness Strength

1st layer(light shade) 20% ≥600Mpa
2nd layer 15% ≥660Mpa
3rd layer 15% ≥730Mpa
4th layer 15% ≥780Mpa
5th layer 15% ≥830Mpa
6th layer 20% ≥900Mpa

Mechanical property:

Sintered Density ≥ 6.0 g/cm³
Bending Strength ≥ 900Mpa
Fracture toughness 5Mpam½
Hardness （Hv 10） 1250
Certification：FDA-America
Certification：ISO13485
Certification：CE
Certification：SFDA-China
Certification：KFDA-South Korea
Certification：PMDA-Japan

Ixion Aligner Pliers are specially designed to prevent distortion of the aligner without the need to heat the plier. The ultra slim tips provide easy access incisally, even with lower anterior aligners.

The Hole Punch Ixion Aligner Plier creates a circular cutout to allow bondable attachments to be used.

Multilayer® 3D

Gradual hardness & Gradual translucency & Gradual color
3D multilayer realizes natural gradient of color,gradient of translucency and gradient of strength in a real sense, achieving another revolution of dental material and revolutionizing dentistry once again！

Color gradient:

6 layers of natural color transition, matching color gradient of natural tooth from cervical to incisal.

Translucency gradient:

Translucency from 57% in incisal to 43% in cervical.It shows gradient decrease,achieving life-like transparency of natural tooth enamel while low transparency in cervical has effective opaque！

Strength gradient:

Strength gradient from 600 Mpa to 900 Mpa. It achieves low strength in occlusion and causes no harm to opposing dentin. High strength in base part realizes long bridge restoration！

Indications:

1) Anterior full contour (crown &bridge)
2) Posterior full contour (crown &bridge)

Color classification:

1) A1 A2 A3 A3.5 A4
2) B1 B2 B3 B4
3) C1 C2 C3 C4
4) D2 D3 D4

Chemical composition and Mechanical property:

1) Sintered Density ≥6g/cm³
2) Fracture Toughness =5Mpam½
3) Hardness(Hv 10) =1250

Flexural strength:

percentage thickness Strength

1st layer(light shade) 20% ≥600Mpa
2nd layer 15% ≥660Mpa
3rd layer 15% ≥730Mpa
4th layer 15% ≥780Mpa
5th layer 15% ≥830Mpa
6th layer 20% ≥900Mpa

Mechanical property:

Sintered Density ≥ 6.0 g/cm³
Bending Strength ≥ 900Mpa
Fracture toughness 5Mpam½
Hardness （Hv 10） 1250
Certification：FDA-America
Certification：ISO13485
Certification：CE
Certification：SFDA-China
Certification：KFDA-South Korea
Certification：PMDA-Japan

Ixion Aligner Pliers are specially designed to prevent distortion of the aligner without the need to heat the plier. The ultra slim tips provide easy access incisally, even with lower anterior aligners.

The Tear Drop Ixion Aligner Plier creates a hook in the gingival margin for the use of elastomerics

Multilayer® 3D

Gradual hardness & Gradual translucency & Gradual color
3D multilayer realizes natural gradient of color,gradient of translucency and gradient of strength in a real sense, achieving another revolution of dental material and revolutionizing dentistry once again！

Color gradient:

6 layers of natural color transition, matching color gradient of natural tooth from cervical to incisal.

Translucency gradient:

Translucency from 57% in incisal to 43% in cervical.It shows gradient decrease,achieving life-like transparency of natural tooth enamel while low transparency in cervical has effective opaque！

Strength gradient:

Strength gradient from 600 Mpa to 900 Mpa. It achieves low strength in occlusion and causes no harm to opposing dentin. High strength in base part realizes long bridge restoration！

Indications:

1) Anterior full contour (crown &bridge)
2) Posterior full contour (crown &bridge)

Color classification:

1) A1 A2 A3 A3.5 A4
2) B1 B2 B3 B4
3) C1 C2 C3 C4
4) D2 D3 D4

Chemical composition and Mechanical property:

1) Sintered Density ≥6g/cm³
2) Fracture Toughness =5Mpam½
3) Hardness(Hv 10) =1250

Flexural strength:

percentage thickness Strength

1st layer(light shade) 20% ≥600Mpa
2nd layer 15% ≥660Mpa
3rd layer 15% ≥730Mpa
4th layer 15% ≥780Mpa
5th layer 15% ≥830Mpa
6th layer 20% ≥900Mpa

Mechanical property:

Sintered Density ≥ 6.0 g/cm³
Bending Strength ≥ 900Mpa
Fracture toughness 5Mpam½
Hardness （Hv 10） 1250
Certification：FDA-America
Certification：ISO13485
Certification：CE
Certification：SFDA-China
Certification：KFDA-South Korea
Certification：PMDA-Japan

K0 korrigeerib valesid harjumusi. K0 on valmistatud elastsest silikoonist, mis sobitub iga kujuga hambakaarega ja viltuste hammastega. Tänu oma elastsusele tagab seade parema retensiooni ka öisel kasutamisel.

The fine tips allow intra oral bending of the archwire. To be used on Nickel Titanium wire up to .020" (.51mm).